Scientific Reports volume 12, Article number: 16307 (2022) Cite this article

2713 Accesses

43 Altmetric

Metrics details

Sodium ion batteries are favored in stationary and large scale power storage due to their low cost and nontoxicity. As the lithium is replaced with sodium due to the cost motive, a cheap processing method is needed to maintain the cell price as low as possible. We report an ultra-fast synthesis method that utilizes the high microwave absorbance of silicon carbide content in rice straw ash. Amorphous/maricite mixtures of sodium iron phosphates-carbon composites (NaFePO4-C) are synthesized, crystallized, and carbon coated using one-step microwave heating. The sodium ion electroactive composites are prepared using different microwave heating durations ranging from 30 to 100 s. High purity inert gases are not needed during synthesis, processing, and even at cell assembly. The materials are characterized by elemental analysis techniques, X-ray diffraction (XRD), scanning/transmission electron microscope (SEM/TEM), and Raman spectroscopy. The electrochemical performance of the synthesized nanocomposites is examined as sodium ion battery cathode and as symmetric supercapacitors. The optimum synthesis time is 60 s for the application as sodium ion batteries and as a supercapacitor. The maximum specific capacity is 108.4 mA h g−1 at 0.2 C in the case of using it as a battery cathode. While the capacitance is 86 F g−1 at 0.5 A g−1 as a supercapacitor. The capacity retention is 92.85% after 40 cycles at 0.2 C as sodium ion battery electrode. For supercapacitor, the capacity retention is 81.7% after 1000 cycles.

Mobile applications such as electric vehicles (EVs), laptops and cell phones have been invaded by lithium ion technologies due to the high specific gravimetric capacities of Li cells1. The lithium depletion fears came early to put the basics of their replacement with sodium ion technologies, especially in stationary and large scale common applications2,3. Sodium has many characteristics that are very close to those of lithium, especially their electronegativity and ionic radius. On the other hand, sodium is environmentally friendly and its abundance in the earth's crust is about 1350 times more than that of lithium4. Many nanomaterials have been revealed as cathodes and anodes for sodium ion batteries (SIBs) and have been published elsewhere5,6,7,8. Sodium vanadium phosphates (NVP) Na3V2(PO4)3 and Na3VCr(PO4)3 with NASICON structures were among the most successful active cathode materials owing to their high and flat discharge potential at 3.4 V vs Na/Na+, which maximizes energy density. They also have the high rate capability advantage due to their sodium ion superconducting open framework structure. However, only two of the three Na+ ions are available at this high potential, resulting in a relatively low theoretical capacity of 118 mA h g−1. In addition, their cost is relatively high9,10. As a raw material, iron oxide is one tenth the cost of vanadium oxide, which lowers the cost advantage of using NVP when compared with LiFePO411. The sodium iron phosphate with its different forms provides a cheap material as sodium ion battery cathodes, in addition to their environmental safety5. Maricite, Olivine, and amorphous forms of NaFePO4, all with a theoretical capacity of 152 mA h g−1, have been explored as active, low cost cathode materials for SIBs12,13,14,15,16. Olivine NaFePO4can be prepared only from LiFePO4 by electrochemical delithiation and subsequent sodiation. It possesses low ionic conductivity due to its one direction Na/Li diffusion tunnels12,17. The conversion of maricite NaFePO4 to amorphous phase was reported by Kim et al. after full de-sodiation, so that, maricite and amorphous NaFePO4 can be considered to have the same electrochemical impact as cathode materials13.

Alkali metal-free transition metal phosphates are attractive materials for symmetric and asymmetric supercapacitors and many reports have been reviewed by Li et al.18. In a limited number of articles, Li/Na transition metal phosphate materials that were originally active as Li/Na ion cathode in batteries have been utilized as an active materials in asymmetric electrochemical supercapacitors. They exhibited good capacitances and excellent cyclic stabilities19,20,21. NaNiPO4 delivered 125 F g−1 when 2 M of NaOH was used as electrolyte and the voltage range was 0–1.6 V20. Sundaram et al. prepared NaMn1/3Co1/3Ni1/3PO4 with Maricite structure, the asymmetric supercapacitor versus carbon that reported a specific capacitance of 40 F g−1 when 1 M NaPF6 in EC/DMC was used as electrolyte and the voltage range was 0–3 V21.

Microwave solid state methods provided a very fast and low-cost route for the synthesis of alkali-transition metal phosphates, especially for production of olivine LiFePO422,23,24. But microwave methods were uncommon for synthesizing Na-transition metal phosphates25,26,27. In this work, sodium iron phosphate is examined as both sodium ion battery and supercapacitor for the first time. The precursor materials cost, the synthesis method cost and the time consumed were greatly minimized by the current procedures. Moreover, a cheaper current collector (Cu foil instead of Ni in the case of supercapacitors) and a dry air filled glove box are used (instead of argon filled glove box). The current work is aiming at lowering the overall battery production cost as much as possible, which is the main target of using sodium ion technologies.

The active materials were synthesized using a microwave carbothermal solid state method. A mixture of 5.01 g Fe3(PO4)2·8H2O (prepared in the laboratory by procedures detailed in supporting information), 0.6 g NaH2PO4 and 2.86 g Na2HPO4 (99.5%, Polskie Odczynniki Chemiczne s.a. Belgium) were ball milled with 3 wt% (0.215 g) of commercial glucose (Anhydrous, ADWIC El-Nasr company, Egypt) and 5wt% (0.355 g) of activated carbon black (ACB) (99.99% VULCAN XC72R,CABOT, USA) at 500 rpm for 30 min in a 50 ml vessel using rotating mode ball milling machine (Fritsch Pulverisette 7, Germany). The ball to powder ratio was 10:1, and the stoichiometry of Na:Fe:P was 3:2:3, (initially designed for the synthesis of NASICON Na3Fe2(PO4)3). For microwave heating, 10 g of previously heat treated rice straw powder was placed in a glass beaker, while a ceramic tube containing 0.8 g of the precursor mixture was immersed in the black rice straw ash powder. The ceramic tube was covered by a 5 ml Wassermann test tube to limit oxygen diffusion during the microwave heating. The microwave reaction setup synthesis process is demonstrated in Fig. 1. A domestic microwave oven (1350 W Thomson, UK) was used to radiate the precursor for 30, 60, 80, and 100 s, then left to cool down to room temperature.

Synthesis process of sodium iron phosphate through ball milling and microwave assisted and assembly of related batteries and supercapacitors.

The elemental composition of the produced NaFePO4/C is analyzed using an ICP-AES instrument (Leeman Labs Prodigy-USA), while carbon content is measured by an HCNS analyzer (ELEMENTAR-Micro VARIO Cube, Germany). Structural analysis is performed using Shimadzu-XRD-6000 Diffractometer, Japan, and Raman spectroscopy (SENTERRA, Bruker, Germany). The morphology is studied using scanning electron microscope (JEOL JSM- 6360 LA SEM, Japan), transmission electron microscope (JOEL, JEM 2100 plus TEM, Japan) attached with a Selected Area Electron Diffraction (SAED) unit, particle size analyzer (Beckman Coulter N5 submicron PSA, USA) and a surface area analyzer (BELSORP-miniX, Germany). For PSA analysis, the powder samples are prepared by dispersing 2 mg of powder in 5 ml of Di-methyl Sulfoxide (DMSO) and sonication in an ultrasonic path for 30 min.

Electrodes are prepared by mixing active materials with conductive carbon (industrial quality graphite nanoplatelets, ACS material, USA) using ball milling at 400 rpm for 30 min. N-methyle pyrrolydone (NMP) (99.5%, Merck, Germany) containing 20 mg ml−1 PVDF (99%, Alfa Aesar, Germany) is added to the mixture. The final weight ratio of (active material:conductive carbon:PVDF) is (75:15:10). The slurry has been plated on Al foil for battery and on Cu foil for supercapacitor applications. The unloaded parts of the current collectors are covered with an isolating tape. The current collectors were weighed before and after material loading. The weight of conductive additive and binder are subtracted to determine the active mass loading in the electrodes.

Electrochemical cells for battery fabrication are composed of the working electrode as a cathode, sodium metal as both the counter and reference electrodes, fiberglass filter paper (GFD Wattman, UK) as a separator and 1 M NaClO4 (99% Across, Germany) in propylene carbonate (PC) (99%, Fluka, Germany) as the electrolyte. Figure 1 shows the synthesis, characterization and components of the used homemade Teflon coin cell. The cells are assembled inside a dry air-filled glove box instead of argon filled glove box, leading to further cost reduction. The symmetric electrochemical capacitors are assembled in air using a GFD separator soaked with saturated Na2SO4 (99% Fischer, Germany) sandwiched between the two similar electrodes.

Cyclic voltammetry, EIS, and charge–discharge tests were performed by two electrode cells using a workstation (Autolab. Aut87070, Germany). Charge–discharge and CV tests were conducted in the range between 1 and 4 V for batteries and between 0.0 and 1.1 V for supercapacitors. EIS measurements were conducted at the initial open circuit potential of the battery, with amplitude of 50 mV, and at a voltage of 50 mV for supercapacitors. The frequency range was from 1 MHz to 0.2 Hz.

Elemental analyses of all synthesized samples are shown in Table S1, giving an approximate atomic ratio of Na, Fe, and P to be nearly 3:2:3, indicating that most water removal and chemical reaction processes took place within the first 30 s of the microwave heating. This may be due to the high loss tangent value of SiC present in the rice straw ash28,29. The remaining carbon content present in samples is 5.4, 4.7, 4.1, and 3.8% for MW heated samples at 30, 60, 80,and 100 s respectively, indicating gradual loss of carbon content as the MW time increases from 30 to 100 s.

The XRD pattern (Fig. 2) shows the formation of maricite phase NaFePO4 (JCPDS card #29-1216) after the first 30 s of the reaction. The maricite crystal structure is orthorhombic with the pmnb space group. The hump present in the graphs indicates a large amount of amorphous phase, which is calculated using Match 3 software according to Eq. (1)30:

(a) XRD patterns of microwave solid state synthesized sodium iron phosphate samples, (b) structure of maricite NaFePO4.

The degrees of crystallinities and crystallite sizes for all samples are summarized in Table1. They indicate the reduction of amorphous phase content with increasing MW time. The crystallite sizes of maricite phase for all samples are calculated from XRD data by applying Scherer’s equation on the (211) and (031) planes. The maximum maricite crystallite size (17.6 nm) is obtained the sample Fe(60). Originally, the reactants stoichiometry was designed for the preparation of NASICON sodium iron phosphate, but the maricite phase has been created beside unreacted species from precursor as Na2HPO4 (JCPDS # 35-0735) or by products as Na3PO4, (PDF#33-1272) according to Eq. (2):

As the temperature increases with increasing MW time over 60 s, a part of the maricite structure reacts with the noninvolved phases (FePO4, Na3PO4) forming other crystalline phases as NASICON (PDF#045-0319) as shown in XRD patterns for Fe(80) and Fe(100) samples. The Fe2P phase usually appears with strong reductive conditions at higher MW durations. This phase has been reported to decrease the ionic conductivity by blocking alkali ion diffusion pathways in olivine LiFePO431.

Graphitic structure starts to appear at 2ϴ around 26.35° and 43.07° corresponding to plans (002) and (101) respectively. With increasing MW duration to 60 s, the intensity of the (002) peak increased due to the graphitization of glucose with broadening and shifting to lower 2ϴ values. With more increase in temperature, graphite layers decrease due to consumption of the remaining diffused oxygen, which can be indicated by a decrease in calculated crystallite sizes of graphite for Fe(80) and Fe(100) samples as shown in Table 1.

Calculated unit cell parameters are listed in Table S2. The dimensions for Fe(60) sample are very close to the theoretical cell parameters of maricite phase. With increasing MW time, a reduction occurs along the a direction while a slight expansion in the b direction takes place. This may occur as a step for incomplete conversion to other phases present in the last MW time Fe(100) such as NASICON and Fe2P. Full conversion to pure NASICON phase during solid state preparation method has been reported at 750 °C for 12 h32.

The Raman spectra of all the prepared samples are presented in Fig. 3.They show four peaks that are characteristic to the vibrational modes of phosphate group. The peaks at around 950 and 1000 cm−1are related to asymmetric and symmetric stretching respectively, while the peaks at around 450, and 600 cm−1 are related to asymmetric and symmetric bending respectively33. The appearances of fingerprint peaks in the region between 200 and 400 cm−1 are characteristic to maricite FeO63− network bending33. Also, the peaks at around 1350, 1600, and 2650 cm−1 are related to D, G, and 2D bands characteristic to carbon coating34. Their numerical intensities decrease as the microwave time increases, which may be due to the consumption of carbon content upon heating. A partial graphitization might take place, forming graphene clusters inside amorphous carbon coating parts. This is indicated by the decrease in the ID/IG ratio to its minimum value of 0.56 at a MW time of 80 s as shown in Table 2. Also, the number of defects may be assumed from the calculation of the ratio of I2D/IG. It gives its minimum value of 0.1 for sample Fe(80) with a maximum crystallite size of 30 nm and the lowest defect content. The crystallite size (La) of graphene clusters in nm is calculated by Eq. (3)35:

where λ is the laser wavelength excitation length of 514.5 nm.

Raman spectra for microwave solid state synthesized sodium iron phosphate samples.

Figure 4 represents a general illustration for SEM, TEM and elemental mapping for samples. Figure 4a–d shows SEM images for all the prepared samples at different MW durations, which possess randomly shaped and sized particles. This could be considered as a common feature for solid stat methods12. Particle size analysis (PSA) shows a wide particle size distribution curve. The mean particle sizes calculated from SEM and PSA are presented in Table 3. Sample Fe(60) has the lowest average size (around 200 nm for PSA and SEM). Surface area of particles measured by BET shows a gradual decrease with increasing MW time due to the graphitization and combination of high surface area ACB particles with sodium iron phosphate particles (Vulcan XC 72 R has a typical surface area of 235 m2 g−136). The measured surface areas and pore diameters are listed in Table 3. The BET and BJH plots are provided with supporting information Figures S2 and S3. The surface area for Fe(60) is 10.1 m2 g−1.The previously reported surface areas for NaFePO4 are range from 3.5 for micro particles to 120 m2 g−1 for 15 nm hollow nanoparticles16,37,38,39. TEM images for the Fe(60) sample show that the graphitized carbon is well distributed on the particle’s surface, but with unequal thickness. The large particles observed in TEM images are composed of small irregular spherical nano-crystallites of about 10–15 nm with an intergranular amorphous matrix as shown in Fig. 4e,f. Selected area electron diffraction (SAED) is shown in the inset of Fig. 4f confirms the presence of a large amount of amorphous phases indicated by continuous circles and a low amount of crystalline phase indicated by plane spots39. Figure 4f,g represent the fast furrier transform (FFT) image and Inverse FFT (IFFT) profile for the selected area, giving d spacing of 1.77 Å for Fe(60) sample along (240) plan. They also indicate the presence of many lattice defects and different growth directions due to the fast microwave heating. Figure 4h,i represent the elemental mapping for the Fe(60) sample, showing the uniform distribution of Na, Fe, P, and O in the selected particles. Carbon coating was also successful and nearly homogenous along the particle’s surface. This homogeneity may be due to the very low size of activated carbon used and the presence of glucose as an additional carbon source.

(a–d) SEM images at ×10,000 for Fe(30), Fe(60), Fe(80) and Fe(100) respectively. (e) Low magnification TEM image showing carbon compositing with NaFePO4 particles, (f) High magnification TEM image and SAED image for NaFePO4 spot, (g) FFT images and IFFT profile of Fe(60) for selected area along (240) plane and (h,i) Elemental mapping showing C, O, Na, Fe, and P distribution on the selected particle.

Figure 5a shows the first discharge profiles of samples at 0.2 C rate. The discharge capacities at different C-rates are listed in Table 4. The best discharge capacity obtained is 108.4 mA h g−1 for Fe(60) sample Vs Na/Na+, which is characterized by the presence of the highest amount of crystalline maricite phase (according to XRD patterns) and the smallest particle size (according to PSA). The order of capacity was Fe(60) > Fe(80) > Fe(100) > Fe(30). For the sample Fe(30), the low capacity may refers to the presence of a large amount of unreacted inactive raw materials. The decrease in capacity with increasing microwave time above 60 s may refer to the decrease in particle size and to the increase in surface area (Table 3). The first charge cycle for all samples exhibits a relatively elevated voltages due to energy consumed during extraction of Na that occupies the corners of the orthorhombic bipyramid in the maricite structure40. As shown in the inset of Fig. 5a, the second charge processes have lower voltages compared to the first. This is because the intercalated Na ions occupy the framework channels in maricite NaFePO4. After the first charge–discharge cycle, maricite NaFePO4 is converted to amorphous phase, so that Na+ ions become easier to extract12,13. Figure 5d shows the difference in XRD pattern before and after cycling, indicating the conversion of the maricite into an amorphous phase. Nyquist plots of samples are presented in Fig. 5c. The RCT values indicate that the sodium ion diffusivity inside the cathode matrix was in the order of Fe(60) > Fe(80) > Fe(100) > Fe(30). Sodium ion diffusion coefficients (DNa) are calculated from the low frequency region according to equation S2 (Supplementary). The calculated values are listed in Table 4. The rate capabilities of samples followed their RCT order, indicating that the enhancement in electronic conductivity of samples is the key factor for improving rate capability. Figure 5,b shows the charge–discharge curves at a different rates for sample Fe(60), the corresponding capacities for other samples are listed in Table 4. Generally, iron based sodium ion batteries suffer from capacity fading with increasing discharge rate41.

(a) First discharge curves showing discharge capacities (at 0.2 C rate) for samples prepared by microwave heating at different times, side graph is the first charge–discharge and 2nd charge cycles at 0.2 C rate for samples Fe(60), showing the first high energy electrochemical sodium extraction process, (b) charge–discharge curves for Fe(60) sample at different C-rates, (c) Nyquist plots of samples prepared at different MW times, side graph shows the equivalent circuit, (d) the XRD patterns of Fe(60) before and after cycling.

Figure 6a shows the galvanic charge discharge curves for prepared materials as symmetric supercapacitor electrode. The value of calculated capacities at discharge currents of 0.5, 1, 1.5, and 2.5 A g−1 are listed in Table 5. The calculations of specific capacitance (C), energy density (E), and power density (P) are based on Eqs. (4), (5), and (6), respectively42,43:

where I is the constant discharge current (A), Δt is the discharge time (sec.), ΔV is the operating potential window (V), m is the mass of the loaded active material on one electrode (g) and Imax is the maximum current used for discharge. The optimized microwave time for this procedure is 60 s. Theoretically, its preferable particle size and surface area are the main factors leading to its high capacity as a supercapacitor. Figure 6b shows the charge–discharge curves of Fe(60) sample at different currents. The values of capacitance show no or little decrease with increasing working current up to 2.5 A g−1 in all samples. This behavior was unexpected for a sodium intercalation material because both mechanisms of insertion-extraction and electrical double layer (EDL) formation should be responsible for charge storage. Here, it is suggested that only the EDL mechanism was included, while the intercalation does not take place because the current densities applied to supercapacitor cells are very high compared to those applied to battery cells (0.2 C-rate is equal to 0.023 A g−1). Figure 6c,d show the capacitive behavior for samples where the area inside the CV curve is indicative of capacitance, (C = Area under the CV curve/2(scan rate × ΔV × m))44. However, the calculations using charge discharge curves are easier and more accurate.

(a) charge discharge curves for samples prepared at different MW durations at 2.5 A g−1, (b) charge discharge curves for Fe(60) sample at different currents, (c) CV curves for samples prepared at different MW times at 200 mV S−1, (d) CV curves for Fe(60) sample at different scan rates, (e) Nyquist plot for samples prepared at different MW durations in an electrochemical capacitor cell. The inset represents the supercapacitor’s equivalent circuit (f) bode phase plot for samples prepared at different MW durations in an electrochemical capacitor cell.

EIS analysis for samples as symmetric supercapacitors shows a small semicircle at the high frequency region (Fig. 6e). The plots confirm the preferable kinetics for Fe(60) sample, since it has the lowest RCT at the high frequency region, the highest slope of straight line at the low frequency region of the Nyquist plot, and the highest phase angle (Fig. 6f), (the ideal supercapacitor theoretically shows a perpendicular line on the Nyquist plot and a phase angle of 90°)42.

The cycling performance of Fe(60) sample was measured as a battery for 100 cycles (Fig. 7a) and as an electrochemical capacitor for 1000 cycles at 2.5 A g−1 (Fig. 7b). As a sodium ion battery, the specific capacity was slightly increased in the 2nd and 3rd cycles. This increase may be due to conversion to an amorphous phase13. The capacity retention was 92.85% after 40 cycles at 0.2 C, 94.7% after the next 20 cycles at 0.5 C, 95.6% after the next 20 cycles at 1 C and 93.5% after the last 20 cycles at 2 C (relative to the capacity of the first cycle at the c-rate start). As an electrochemical capacitor, the capacity retention after 1000 cycles was only 41.8%, and most of the capacitance loss occurs in the first 200 cycles.

(a) Cyclic performance of Fe(60) sample in Na-ion cell at different C rates. (b) Cyclic performance of Fe(60) sample as symmetric electrochemical capacitor in different electrolytes, (c) cycles 50–55 of Fe(60) sample cycling test with saturated Na2SO4 and (d) electrodes after 1000 cycles using different electrolytes.

It was noticed that the active material is eroding in the neutral electrolyte that becomes slightly acidic at the negative electrode45. The acidic media increase the solubility of iron phosphates. Formation of iron III sulfate and sodium phosphate in electrochemical reaction is another possible reason for dissolution as an explanation for cathode material erosion. Figure 7d shows the difference between positive and negative similar electrodes after 1000 cycles using saturated Na2SO4, indicating gradual dissolution of active material at the negative electrode in the electrolyte. The cycling test was conducted using 2 M NaOH and a mixture of 1 M NaOH with saturated Na2SO4 as electrolyte. The active material shows more stability in the two basic electrolytes as shown in Fig. 7c and enhanced cycle retention, indicating that the acidic dissolution mechanism is more likely responsible for active material corrosion. For 2 M NaOH cells, the recorded initial capacitance was only 53.6 F g−1 at current 2.5 A g−1 and about 81.7% of capacity was retained after 1000 cycles. For NaOH/Na2SO4 cells, an initial capacitance of 81.8 F g−1 is obtained with capacity retention of 68.3% after 1000 cycles at 2.5 A g−1.

When comparing battery performance to other works, this work is in the middle region of the recorded capacities and rate capabilities. On the other hand, the time and cost of energy consumed for synthesis are incomparable. Table S3 summarizes a comparison between our study and other prepared cathode materials. The comparison includes the difference in preparation methods and time consumed for each preparation step.

When comparing electrochemical capacitor performance, we concluded that the capacitance does not increase due to the intercalation ability of maricite/amorphous sodium iron phosphate, resulting in uncompetitive capacity. In addition, this work requires further enhancement in cyclic performance and durability of active materials. However, the investigation of supercapacitive ability was limited to Ni and Co phosphates18. To the best of our knowledge, this is the first report that uses this method for synthesis of maricite/amorphous NaFePO4 and the first report that investigates NaFePO4 as a symmetric electrochemical capacitor.

Sodium iron phosphate–carbon nanocomposites were prepared by an ultrafast microwave technique. Egyptian rice straw ash as MW absorber enabled the synthesis in a very short time and with low cost process. This fast MW heating with the presence of slightly reductive conditions replaced the need for argon gas in the synthesis, crystallization, and carbon coating processes, which are done in a one step. In addition, this method has a high degree of flexibility to use many sodium, transition metal, phosphate, and carbon sources, which enables many available modifications and optimization factors to enhance capacity, rate capability, and cyclic performance. The downside of this method is the irregular and non-uniform shape and size of the produced particles. The materials produced by the microwave are a polymorphic NaFePO4 with a small crystallite size. The fast heating does not allow the crystal growth to be completed and the 10–15 nm particle size is obtained, as evidenced by TEM. However, the particles tend to agglomerate, forming larger grains with an average size of about 300 nm, which limits the sodium ion diffusivity. So, the produced active materials showed good electrochemical activity as a battery with a capacity of 108.4 mA h g−1, with a moderate rate capability, and good cyclic stability. As a supercapacitor, the capacitance was 86.3 F g−1 and showed cyclic stability in alkaline electrolytes with capacity retention of 81.7% of capacity after 1000 cycles at 2.5 A g−1, which could be useful in short-term general applications.

All data generated or analysed during this study are included in this published article [and its supplementary information files].

Li, X. et al. Review on comprehending and enhancing the initial Coulombic efficiency of anode materials in lithium-ion/sodium-ion batteries. Nano Energy 77, 105143. https://doi.org/10.1016/j.nanoen.2020.105143 (2020).

Article CAS Google Scholar

Palomares, V. et al. Na-ion batteries, recent advances and present challenges to become low cost energy storage systems. Energy Environ. Sci. 5(3), 5884–5901. https://doi.org/10.1039/c2ee02781j (2012).

Article CAS Google Scholar

Liu, Q. et al. The cathode choice for commercialization of sodium-ion batteries: Layered transition metal oxides versus Prussian Blue analogs. Adv. Funct. Mater. 30, 14. https://doi.org/10.1002/adfm.201909530 (2020).

Article CAS Google Scholar

http://www.webelements.com/webelements/properties/text/image-group-1/abund-crust.html.

Jin, T. et al. Polyanion-type cathode materials for sodium-ion batteries. Chem. Soc. Rev. 49(8), 2342–2377. https://doi.org/10.1039/c9cs00846b (2020).

Article CAS PubMed Google Scholar

Shen, Q., Liu, Y., Jiao, L., Qu, X. & Chen, J. Current state-of-the-art characterization techniques for probing the layered oxide cathode materials of sodium-ion batteries. Energy Storage Mater. 35, 400–430. https://doi.org/10.1016/j.ensm.2020.11.002 (2021).

Article Google Scholar

He, H., Sun, D., Tang, Y., Wang, H. & Shao, M. Understanding and improving the initial Coulombic efficiency of high-capacity anode materials for practical sodium ion batteries. Energy Storage Mater. 23, 233–251. https://doi.org/10.1016/j.ensm.2019.05.008 (2019).

Article Google Scholar

Wazeer, W., Nabil, M., Feteha, M., Soliman, M. & Kashyout, A. E. Alkali etched nanoporous silicon graphene composite as sodium ion battery anode. Int. J. Mater. Technol. Innov. https://doi.org/10.21608/ijmti.2021.101079.1040 (2021).

Article Google Scholar

Huang, X. et al. Outstanding electrochemical performance of N/S co-doped carbon/Na3V2(PO4)3 hybrid as the cathode of a sodium-ion battery. Ceram. Int. https://doi.org/10.1016/j.ceramint.2020.07.303 (2020).

Article Google Scholar

Zhao, Y., Gao, X., Gao, H., Jin, H. & Goodenough, J. B. Three electron reversible redox reaction in sodium vanadium chromium phosphate as a high-energy-density cathode for sodium-ion batteries. Adv. Funct. Mater. 30, 10. https://doi.org/10.1002/adfm.201908680 (2020).

Article CAS Google Scholar

United States Geological Survey (USGS), Mineral Commodity Summaries 2020, no. 703. 2020.

Prosini, P. P., Cento, C., Masci, A. & Carewska, M. Sodium extraction from sodium iron phosphate with a Maricite structure. Solid State Ion. 263, 1–8. https://doi.org/10.1016/j.ssi.2014.04.019 (2014).

Article CAS Google Scholar

Kim, J. et al. Unexpected discovery of low-cost maricite NaFePO4 as a high-performance electrode for Na-ion batteries. Energy Environ. Sci. 8(2), 540–545. https://doi.org/10.1039/c4ee03215b (2015).

Article CAS Google Scholar

Oh, S. M., Myung, S. T., Hassoun, J., Scrosati, B. & Sun, Y. K. Reversible NaFePO4 electrode for sodium secondary batteries. Electrochem. Commun. 22(1), 149–152. https://doi.org/10.1016/j.elecom.2012.06.014 (2012).

Article CAS Google Scholar

Zheng, M. Y. et al. Anionic redox processes in maricite- and triphylite-NaFePO4 of sodium-ion batteries. ACS Omega 5(10), 5192–5201. https://doi.org/10.1021/acsomega.9b04213 (2020).

Article CAS PubMed PubMed Central Google Scholar

Li, C., Miao, X., Chu, W., Wu, P. & Tong, D. G. Hollow amorphous NaFePO4 nanospheres as a high-capacity and high-rate cathode for sodium-ion batteries. J. Mater. Chem. A 3(16), 8265–8271. https://doi.org/10.1039/c5ta01191d (2015).

Article CAS Google Scholar

Zhu, Y., Xu, Y., Liu, Y., Luo, C. & Wang, C. Comparison of electrochemical performances of olivine NaFePO4 in sodium-ion batteries and olivine LiFePO4 in lithium-ion batteries. Nanoscale 5(2), 780–787. https://doi.org/10.1039/c2nr32758a (2013).

Article ADS CAS PubMed Google Scholar

Li, X., Elshahawy, A. M., Guan, C. & Wang, J. Metal phosphides and phosphates-based electrodes for electrochemical supercapacitors. Small 13, 39. https://doi.org/10.1002/smll.201701530 (2017).

Article CAS Google Scholar

Xie, Y., Song, F., Xia, C. & Du, H. Preparation of carbon-coated lithium iron phosphate/titanium nitride for a lithium-ion supercapacitor. New J. Chem. 39(1), 604–613. https://doi.org/10.1039/c4nj01169d (2015).

Article CAS Google Scholar

Minakshi, M. et al. Synthesis, structural and electrochemical properties of sodium nickel phosphate for energy storage devices. Nanoscale 8(21), 11291–11306. https://doi.org/10.1039/c6nr01179a (2016).

Article ADS CAS PubMed Google Scholar

Sundaram, M. M. et al. Synthesis, and crystal and electronic structure of sodium metal phosphate for use as a hybrid capacitor in non-aqueous electrolyte. Dalt. Trans. 44(46), 20108–20120. https://doi.org/10.1039/c5dt03394b (2015).

Article CAS Google Scholar

Higuchi, M., Katayama, K., Azuma, Y., Yukawa, M. & Suhara, M. Synthesis of LiFePO4 cathode material by microwave processing. J. Power Sources 119(121), 258–261. https://doi.org/10.1016/S0378-7753(03)00243-X (2003).

Article ADS CAS Google Scholar

Beninati, S., Damen, L. & Mastragostino, M. MW-assisted synthesis of LiFePO4 for high power applications. J. Power Sources 180(2), 875–879. https://doi.org/10.1016/j.jpowsour.2008.02.066 (2008).

Article ADS CAS Google Scholar

Guo, X. F., Zhan, H. & Zhou, Y. H. Rapid synthesis of LiFePO4/C composite by microwave method. Solid State Ion. 180(4–5), 386–391. https://doi.org/10.1016/j.ssi.2008.11.021 (2009).

Article CAS Google Scholar

Güler, H. & Kurtuluş, F. A rapid synthesis of sodium titanium phosphate, NaTi2(PO4)3 by using microwave energy. Mater. Chem. Phys. 99(2–3), 394–397. https://doi.org/10.1016/j.matchemphys.2005.11.011 (2006).

Article CAS Google Scholar

Costa, D. A. S. et al. Microwave assisted ultra-fast method to synthesize carbonate-phosphates, Na3MCO3PO4 (M = Mn, Fe Co, Ni) - Relevant materials applied in sodium-ion batteries. J. Braz. Chem. Soc. 31(1), 175–185. https://doi.org/10.21577/0103-5053.20190154 (2020).

Article CAS Google Scholar

Gutierrez, A., Kim, S., Fister, T. T. & Johnson, C. S. Microwave-assisted synthesis of NaCoPO4 red-phase and initial characterization as high voltage cathode for sodium-ion batteries. ACS Appl. Mater. Interfaces 9(5), 4391–4396. https://doi.org/10.1021/acsami.6b14341 (2017).

Article CAS PubMed Google Scholar

Ramesh, P. D., Brandon, D. & Schächter, L. Use of partially oxidized SiC particle bed for microwave sintering of low loss ceramics. Mater. Sci. Eng. A 266(1–2), 211–220. https://doi.org/10.1016/s0921-5093(99)00017-9 (1999).

Article Google Scholar

Patel, M. & Kumari, P. Silicon carbide from sugarcane leaf and rice straw. J. Mater. Sci. Lett. 9(4), 375–376. https://doi.org/10.1007/BF00721002 (1990).

Article CAS Google Scholar

Hisbiyah, A., Nisyak, K., Prasetya, Y. A., Iftitah, E. D. & Srihardyastutie, A. Synthesis of zno-Ag nanocomposites trough ultrasonication-microwave combination method with clove leaf oil. IOP Conf. Ser. Mater. Sci. Eng. 833, 1. https://doi.org/10.1088/1757-899X/833/1/012070 (2020).

Article Google Scholar

Song, M. S. et al. Amphoteric effects of Fe2P on electrochemical performance of lithium iron phosphate-carbon composite synthesized by ball-milling and microwave heating. J. Power Sources 180(1), 546–552. https://doi.org/10.1016/j.jpowsour.2008.01.079 (2008).

Article ADS CAS Google Scholar

Rajagopalan, R. et al. Improved reversibility of Fe3+/Fe4+ redox couple in sodium super ion conductor type Na3Fe2(PO4)3 for sodium-ion batteries. Adv. Mater. 29, 12. https://doi.org/10.1002/adma.201605694 (2017).

Article CAS Google Scholar

Xiong, F. et al. Revealing the atomistic origin of the disorder-enhanced Na-storage performance in NaFePO 4 battery cathode. Nano Energy 57, 608–615. https://doi.org/10.1016/j.nanoen.2018.12.087 (2019).

Article CAS Google Scholar

Lazzarini, A. et al. A comprehensive approach to investigate the structural and surface properties of activated carbons and related Pd-based catalysts. Catal. Sci. Technol. 6(13), 4910–4922. https://doi.org/10.1039/c6cy00159a (2016).

Article CAS Google Scholar

Liu, W. W., Chai, S. P., Mohamed, A. R. & Hashim, U. Synthesis and characterization of graphene and carbon nanotubes: A review on the past and recent developments. J. Ind. Eng. Chem. 20(4), 1171–1185. https://doi.org/10.1016/j.jiec.2013.08.028 (2014).

Article CAS Google Scholar

Maiyalagan, T., Alaje, T. O. & Scott, K. Highly stable Pt-Ru nanoparticles supported on three-dimensional cubic ordered mesoporous carbon (Pt-Ru/CMK-8) as promising electrocatalysts for methanol oxidation. J. Phys. Chem. C 116(3), 2630–2638. https://doi.org/10.1021/jp210266n (2012).

Article CAS Google Scholar

Yadav, S. N., Rajoba, S. J., Kalubarme, R. S., Parale, V. G. & Jadhav, L. D. Solution combustion synthesis of NaFePO4 and its electrochemical performance. Chin. J. Phys. 69(November 2020), 134–142. https://doi.org/10.1016/j.cjph.2020.11.020 (2021).

Article CAS Google Scholar

Chen, M. et al. NASICON-type air-stable and all-climate cathode for sodium-ion batteries with low cost and high-power density. Nat. Commun. 10, 1. https://doi.org/10.1038/s41467-019-09170-5 (2019).

Article ADS CAS Google Scholar

Abd El-Lateef, H. M., Touny, A. H. & Saleh, M. M. Synthesis of crystalline and amorphous iron phosphate nanoparticles by simple lowerature method. Mater. Res. Express 6, 3. https://doi.org/10.1088/2053-1591/aaf82b (2019).

Article CAS Google Scholar

Zaghib, K. et al. Characterization of Na-based phosphate as electrode materials for electrochemical cells. J. Power Sources 196(22), 9612–9617. https://doi.org/10.1016/j.jpowsour.2011.06.061 (2011).

Article ADS CAS Google Scholar

Zhu, X. et al. A new sodium iron phosphate as a stable high-rate cathode material for sodium ion batteries. Nano Res. 11(12), 6197–6205. https://doi.org/10.1007/s12274-018-2139-0 (2018).

Article CAS Google Scholar

Elessawy, N. A., El Nady, J., Wazeer, W. & Kashyout, A. B. Development of high-performance supercapacitor based on a novel controllable green synthesis for 3D nitrogen doped graphene. Sci. Rep. 9, 1. https://doi.org/10.1038/s41598-018-37369-x (2019).

Article CAS Google Scholar

Moustafa, E., El Nady, J., Kashyout, A. E. H. B., Shoueir, K. & El-Kemary, M. Fabrication of high yield photoluminescent quantized graphene nanodiscs for supercapacitor devices. ACS Omega https://doi.org/10.1021/acsomega.1c02277 (2021).

Article PubMed PubMed Central Google Scholar

Wang, K., Wu, H., Meng, Y., Zhang, Y. & Wei, Z. Integrated energy storage and electrochromic function in one flexible device: An energy storage smart window. Energy Environ. Sci. 5(8), 8384–8389. https://doi.org/10.1039/c2ee21643d (2012).

Article CAS Google Scholar

Kuhn, A. T. & Chan, C. Y. pH changes at near-electrode surfaces. J. Appl. Electrochem. 13(2), 189–207. https://doi.org/10.1007/BF00612481 (1983).

Article CAS Google Scholar

Download references

Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).

Electronic Materials Department, Advanced Technology and New Materials Research Institute, City of Scientific Research and Technological Applications (SRTA-City), P.O. Box 21934, New Borg El-Arab City, Alexandria, Egypt

Wael Wazeer, Marwa M. Nabil & Abd El-Hady B. Kashyout

Materials Science Department, Institute of Graduate Studies and Research, Alexandria University, 163 Horrya Avenue, Shatby, P.O. Box 832, Alexandria, 21526, Egypt

Mohamed Feteha & Moataz B. Soliman

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

All authors have an equal contribution in writing, editing, and revision.

Correspondence to Wael Wazeer or Abd El-Hady B. Kashyout.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Wazeer, W., Nabil, M.M., Feteha, M. et al. Ultra-fast green microwave assisted synthesis of NaFePO4-C nanocomposites for sodium ion batteries and supercapacitors. Sci Rep 12, 16307 (2022). https://doi.org/10.1038/s41598-022-20329-x

Download citation

Received: 20 March 2022

Accepted: 12 September 2022

Published: 29 September 2022

DOI: https://doi.org/10.1038/s41598-022-20329-x

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative