Scientific Reports volume 5, Article number: 17773 (2016) Cite this article

3097 Accesses

33 Citations

Metrics details

High-ordered anatase TiO2 nanotube array films coated with exposed high-reactive {001} nanofacets were fabricated by a modified hydrothermal method using amorphous anodic TiO2 nanotube arrays (ATONAs) as starting materials. It was found that the reaction between gas phase HF and solid ATONAs played a key role in the transformation process from amorphous to anatase TiO2 and the TiO2 tubular structure kept unchanged during the surface modification with an exposed {001} facets up to 76.5%, which could be attributed to the low reaction temperature of 130 °C. Our study provided a novel route for the facile preparation of {001} facets exposed anatase TiO2.

Anatase TiO2 nanotube array films coated with exposed {001} nanofacets have been synthesized by a modified hydrothermal method.

Anatase TiO2 with 76.5% of exposed {001} facets was achieved at temperature as low as 130 °C.

A novel reaction route between HF gas and solid ATONAs played a key role.

The transformation depended on solid state atomic rearrangement.

Among the three main titanium dioxide (TiO2) polymorphs, anatase TiO2 has attracted much attention because of its unique electronic, optical and catalytic properties1,2,3, which showed various applications such as photocatalysis, photovoltaics, drug delivery, hydrogen production and lithium ion batteries4,5,6,7. Recently, the synthesis and application of anatase TiO2 with exposed {001} facets have been a hot topic8. Both theoretical and experimental studies revealed that the exposed (001) surfaces showed much higher chemical activities than the (101) surfaces in anatase TiO2 crystals8,9,10. Therefore, it is desirable to prepare TiO2 crystals with more reactive {001} facets exposed. Hydrothermal synthesis with F− has been proven to be the most frequently used and the most effective method8,9,10,11,12,13. The main procedures for the exposal of {001} planes of anatase TiO2 included two steps: (i) the preparation of low surface energy {001} planes by terminating the dangling bonds with F−, at this stage, the photocatalytic activity of the TiO2 is still low; (ii) the removal of surface F− by 600 °C annealing which produced F− free exposed {001} planes. Note that the first step is essential for the exposal of {001} nanofacets. Up to now, a reaction temperature at least 200 °C is necessary for the hydrothermal preparation of anatase TiO2 with exposed {001} facets8,9,10,11,12,13.

Herein, we found that by using a modified hydrothermal method, which avoided the direct contact of ATONAs with HF solution13,14,15, thus the reaction between gas phase HF (but not acid HF solution) and solid ATONAs played a key role in the transformation process from amorphous to anatase TiO2 and TiO2 nanotube array films with exposed {001} facets up to 76.5% was successfully prepared at reaction temperature as low as 130 °C. After the surface F− ions were removed by 2 h of 600 °C annealing8,13,16, the obtained F− free TiO2 films with exposed {001} nanofacets showed much better photocatalytic activities than the original ATONAs for methyl orange (MO) degradation.

Figure 1a,b shows the XRD patterns of the as-synthesized samples with different preparation conditions. For ATONAs, only diffraction peaks of titanium were detected, indicating that the as grown ATONAs have amorphous structure17. After hydrothermal treatment, broad diffraction peaks at 25.3°, 37.8°, 48.2°, 53.9° and 55.2° were observed, which can be indexed to the (101), (004), (200), (105) and (211) reflections of anatase TiO2 and the diffraction peak intensities at 25.3° and 37.8° increased with preparation time, indicating the nucleation and growth of anatase TiO2 during 130 °C hydrothermal treatment (the XRD patterns of samples for 1.5 h and 2 h were shown in Fig. S1 in Supporting Information). Note that, the appearance of strong peak at 37.8°, which was attributed to (004) planes of anatase TiO2, suggested the presence of exposed {001} nanofacets18. Especially for H-16 and H-20 (Fig. 1b), the exposed {001} planes was estimated to be as high as 74.5% and 76.5%, respectively19. The EDS spectra in Fig. 1c indicated that the surface F− ions were completely removed by 600 °C annealing8,13,16. XPS measurement also confirmed the successful removal of the surface F− species, as shown in Fig. 1d. At the same time, diffraction peaks attributed to {101} planes sharpened, while the (004) peak at 37.8° weakened slightly, indicating that the loss of terminated F− preferred the exposal of {101} planes. The average grain size estimated from FWHM of diffraction peaks at 25.3° and 37.8° was 12.2 nm and 34.1 nm for H-16 and 30.6 nm and 29.3 nm for HT-16, respectively as shown in Fig. 1e. By the way, the post annealing also induced the formation of rutile nanoparticles, as a result, diffraction peaks of 27.5°, 36.1°, 39.3° and 54.3° appeared20,21.

(a) and (b) XRD patterns of the samples before and after post annealing. The red dot circle is the location of (004) planes of the anatase TiO2. (c) EDS patterns of sample before (H-0.5 and H-1.5) and after (HT-0.5 and HT-1.5) post annealing, the red dot circle is the position of F Kα. (d) XPS spectra of two samples before and after post annealing, which clearly showed that the surface F– ions were removed by annealing. (e) Structural information of the synthesized samples. SH-101 and SH-004: the average particle sizes calculated from the FWHM of (101) and (004) peak for samples before post annealing; SHT-101 and SHT-004: the average particle sizes calculated from the FWHM of (101) and (004) peak for samples after annealing; PH-004 and PHT-004: the percentage of exposed {001} nanofacets before and after annealing.

Figure 2 shows SEM images of samples prepared under different conditions. The inset of Fig. 2a is SEM image showing the morphology of the as-prepared ATONAs, which were highly ordered and were grown vertically to the titanium substrate. Figure 2a is the ATONAs after 0.5 h hydrothermal treatment, the tubular structure was maintained with small particles coated on the surface (~8 nm estimated from the FWHM of peak at 25.3°). Even the hydrothermal treatment time increased to 20 h, the tubular structure still kept unchanged as the cross section image shown in Fig. 2e. Amazingly, after 600 °C annealing, the surface coated nanoparticles grew up to be nanofacet like grains (insets of Fig. 2d,f ) and the tubular structure was still maintained as shown in Fig. 2b,d,f, which provided an extremely large surface area compared to the normal TiO2 films (low-magnification SEM images were shown in Figs. S2 to S6).

Typical SEM images of the samples: (a) H-0.5, (b) HT-0.5, (c) H-16, (d) HT-16, (e) H-20, (f) HT-20. The inset in (a) is as-prepared ATONAs and other insets are morphology of film surface. And their low-magnification images are represented in ESI.

Figure 3a shows SEM image of nanoparticles with truncated bipyramidal or trapezoidal shapes and even some with cubic morphology of anatase TiO2 coated on the surface of HT-2, which could be attributed to different degree of truncated octahedral. Figure 3b shows typical TEM image of some nanoparticles, which have regular facet-like geometry with exposed flat square22. All SEM and TEM images indicated the successful exposal of F− free (004) planes after annealing8. Figure 1e summarized the grain size and the evaluation of percentage of exposed {001} planes, according to early estimation method19,23,24, TiO2 with exposed {001} facets up to 76.5% was successfully prepared.

(a) SEM and (b) TEM image of HT-2. The inset is a model of equilibrium shape of anatase TiO2 with exposed {101} and {001}.

Figure 4a shows the HRTEM image of H-2 sample, nanoparticles with grain size in the orders of several nanometers could be observed, the crystal lattice with a spacing of 0.235 nm (004) and 0.35 nm (101) confirmed the anatase TiO2 nanoparticles24. Moreover, the observed (004) planes are parallel to the particle surface, which presented direct evidence for the existence of {001} exposed nanofacets. Evidently, the amorphous ATONAs partially transformed into anatase TiO2 with exposed {001} nanofacets by hydrothermal treatment at 130 °C. Figure 4b is a typical HRTEM image of HT-2, in this selected observation window, almost all grains had spacing of 0.235 nm (parallel to the grain surface); indicated the high percentage of exposed {001} planes. By the way, a rutile TiO2 grain with a spacing of 0.229 nm belonging to (200) planes was also detected, consistent with XRD results shown in Fig. 1. HRTEM images of HT-20 were shown in Fig. S7.

HRTEM images of (a) H-2 and (b) HT-2. The 0.235 nm and 0.35 nm are the distances between (004) planes and (101) plane of anatse TiO2, respectively. The 111.7° is the angle between (004) plane and (101) plane of anatase TiO2.

Normally, anatase TiO2 grains are dominated by {101} facets rather than {001} facets, the latter is more active but with high surface energy25,26,27,28,29. When the surface was terminated with F−, the expose of {001} is energetically preferable to {101} and this was proven theoretically and experimentally by using hydrothermal method8,9,10, by which the Ti precursors were directly immersed into F−/HF containing solutions30. A dissolution-precipitation or dissolution-recrystallization process was proposed to describe the transformation from {101} to {001} facets31,32,33. Here we modified the hydrothermal method by separating the ATONAs from the acid HF solution30, accordingly, the reaction between gas phase HF and solid ATONAs becomes the only route for the transformation from amorphous to anatase TiO2. From the XRD spectra shown in Fig. 1, a low temperature of 130 °C was enough to induce this transformation. This could be attributed to the use of amorphous TiO2 as starting materials, which reduced the activation energy for atom rearrangement. The tubular structure of ATONAs was kept unchanged after hydrothermal treatment, which provided additional evidence that this transformation could not be explained through dissolution-precipitation or dissolution-recrystallization process, which destroyed the initial tubular structure31,32,33. The driving force for this transformation could be the surface energy change caused by F− termination and {001} nanofacets were preferred finally8,9,10,11,12,13,14. From literature, the solid state transformation via atomic rearrangement in amorphous matrix is frequently proposed34,35. And the synthesis of anatase TiO2 with exposed {001} facets by heat treatment (450 °C) using amorphous ATONAs as starting materials was achieved13,16. Here we demonstrated that a solid-state phase transformation from TiO2 {101} to {001} facets could be achieved at a low temperature of 130 °C.

After the surface F− ions were removed by 600 °C post annealing, F− free {001} facets with high reactivity were achieved. Figure 5a shows the photocatalytic activities of ATONAs, HT-0.5, HT-1.5, HT-16 and HT-20, respectively. The corresponding degradation efficiency increased with the percentage of {001} nanofacets and more than 97% of MO could be removed in 90 min over HT-16 and HT-20. According to Langmuir-Hinshelwood model36, the reaction rate coefficient k of HT-20 (k6 = 3.83 × 10−2 min−1) is 150 times higher than that of ATONAs (k1 = 2.45 × 10−4 min−1) (Fig. 5b), which demonstrated the excellent photocatalytic activities of TiO2 nanotube array films with exposed {001} nanofacets obtained in this study, coincided well with earlier reports13,15.

Photocatalytic activities of ATONAs, HT-0.5, HT-1.5, HT-2, HT-16 and HT-20 (a) and their corresponding pseudo-first-order kinetics (b).

In summary, anatase TiO2 nanotube array films with exposed {001} nanofacets were successfully prepared by a modified low-temperature hydrothermal method at 130 °C. The novel reaction route between gas phase HF and solid ATONAs was demonstrated which played a key role for the solid state transformation process from amorphous to anatase TiO2, after the surface dangling bonds were terminated with F− ions, {001} facets became energetically favored. F− free {001} facets with high reactivity could be achieved via 600 °C post annealing. The prepared anatase TiO2 nanotube array films with exposed {001} nanofacets exhibited enhanced photocatalytic activity for methyl orange (MO) degradation under ultraviolet light (UV), which could be attributed to the improvement of charge separation derived from the synergy effect between {001} and {101} facets.

All reagents (Sinopharm, analytical grade, Shanghai, China) were used without further purification. Well-aligned ATONAs on a Ti substrate were fabricated via traditional electrochemical anodization37. Briefly, the anodic growth was conducted using a home-made two electrode electrochemical cell under a constant voltage of 40 V at room temperature, titanium plates (Ti, 90 mm × 40 mm × 0.2 mm, 99.9% purity, Baoji, Shanxi, China) were used as working electrode and a graphite plate as the counter electrode, the electrolyte was composed of 3 wt% NH4F and 0.5 v% H2O dissolved in the ethylene glycol. The obtained well-aligned ATONAs were rinsed with ethylene glycol and ethanol to remove the residual electrolyte solution followed by drying at 80 °C for later use (inset of Fig. 2a).

The well-aligned ATONAs were treated at 130 °C in an autoclave. In a typical experiment, 6 ml of hydrofluoric acid solution with pH = 3 was transferred to a Teflon-lined autoclave (capacity: 25 mL), then the as-synthesized ATONAs, which were cut into 2 cm × 2 cm dices, were fixed by Teflon holders 1 cm above the solution to avoid dipping the ATONAs into the solution. Then, the autoclave was sealed and heated at 130 °C for 0.5 h to 20 h. After the autoclave was cooled down to room temperature, the products were washed with ethylene glycol, ethanol and deionized water and then dried in an oven at 80 °C for 0.5 h, the samples were labeled as H-t (where t stood for the hydrothermal time). Then, samples were heated at 600 °C for 2 h in air with a heating rate of 2°/min to obtain {001} nanofacets exposed films and the final samples were labeled as HT-t.

X-ray diffraction (XRD) patterns were recorded on a Philips XD-98 X-ray diffractometer with Cu Kα radiation (λ = 0.15406 nm). The morphology of the samples was characterized by A ZEISS ULTRA 55 scanning electron microscopy (SEM) equipped with energy dispersive spectrometer (EDS) and transmission microscopy (TEM, FEI Tecnai G2 F20 S-TWIN, FEI Inc., America). X-ray photoelectron spectroscopy (XPS) data were obtained using a Thermo ESCALAB 250Xi (Thermo Fisher Scientific), the X-ray source was an Al Kα radiation and all binding energies were referenced to the 284.8 eV C1s.

The photocatalytic activities were evaluated by degrading the methyl orange (MO, 0.15 mg/L) as the model organic pollutants in aqueous solutions, three plates of {001} exposed TiO2 films (size: 2 cm × 2 cm, TiO2 weight: ca. 1.8 mg) were dipped in 30 mL of MO solution and then were irradiated by a 125 W mercury lamp which irradiated the light of 365 nm. Before irradiation, the system was put in a darkroom for 0.5 h with magnetic stirring to ensure adsorption and desorption equilibrium between the samples and organic molecules. The photodegradation experiments were performed in an open quartz vessel under continuously stirring. During degradation, 2 mL of MO were taken every 30 min and the concentration of MO was measured by UV-3600 spectrophotometer (Shimadzu, Japan) at 463 nm38. The influence of sampling was compensated in degradation efficiency calculation.

How to cite this article: Ding, J. et al. Low-temperature synthesis of high-ordered anatase TiO2 nanotube array films coated with exposed {001} nanofacets. Sci. Rep. 5, 17773; doi: 10.1038/srep17773 (2015).

Burda, C. et al. Enhanced nitrogen doping in TiO2 nanoparticles. Nano Lett. 3, 1094–1051 (2003).

Article Google Scholar

Chatterjee, D. & Dasgupta, S. Visible light induced photocatalytic degradation of organic pollutants. J. Photochem. Photobiol. C 6, 186–205 (2005).

Article CAS Google Scholar

Chen, X. B. & Mao, S. S. Titanium dioxide nanomaterials: synthesis, properties, modifications and applications. Chem. Rev. 107, 2891–2959 (2007).

Article CAS Google Scholar

Fujishima, A. & Honda, K. Electrochemical photolysis of water at a semiconductor electrode. Nature 238, 37–38 (1972).

Article CAS ADS Google Scholar

Han, H. et al. Dominant factors governing the rate capability of a TiO2 nanotube anode for high power lithium ion batteries. ACS Nano 6, 8308–8315 (2012).

Article CAS Google Scholar

Habisreutinger, S. N., Schmidt-Mende, L. & Stolarczyk, J. K. Photocatalytic reduction of CO2 on TiO2 and other semiconductors. Angew. Chem. Int. Ed. 52, 7372–7408 (2013).

Article CAS Google Scholar

Sarkar, D., Ghosh, C. K., Mukherjee, S. & Kalyan, K. C. Three dimensional Ag2O/TiO2 type-II (p-n) nanoheterojunctions for superior photocatalytic activity. ACS Appl. Mater. Interfaces 5, 331–337 (2013).

Article CAS Google Scholar

Yang, H. G. et al. Anatase TiO2 single crystals with a large percentage of reactive facets. Nature 453, 638–641 (2008).

Article CAS ADS Google Scholar

Pan, X. Y., Zhang, N., Fu, X. Z. & Xu, Y. J. Selective oxidation of benzyl over TiO2 nanosheets with exposed {001} facets: catalyst deactivation and regeneration. Appl. Catal. B 453, 181–187 (2013).

Article CAS Google Scholar

Roy, N., Sohn, Y. & Pradhan, D. Synergy of low-energy {101} and high-energy {001} TiO2 crystal facets for enhanced photocatalysis. ACS Nano 7, 2532–2540 (2013).

Article CAS Google Scholar

Wen, C. Z. et al. Synthesis of micro-sized titanium dioxide nanosheets wholly exposed with high-energy {001} and {100} facets. Chem. Commun. 47, 4400–4402 (2011).

Article CAS Google Scholar

Ong, W. J., Tan, L. L., Chai, S. P., Yong, S. T. & Mohamed, A. R. Highly reactive {001} facets TiO2–based composites: synthesis, formation mechanism and characterization. Nanoscale 6, 1946–2008 (2014).

Article CAS ADS Google Scholar

Liao, Y. L. et al. Activating the single-crystal TiO2 nanoparticle film with exposed {001} facets. ACS Appl. Mater. Interfaces 5, 6463–6466 (2013).

Article CAS Google Scholar

Wang, X. N. et al. Synthesis of anatase TiO2 tubular structures microcrystallites with a high percentage of {001} facets by a simple one-step hydrothermal template process. Chem. Eur. J. 16, 7106–7109 (2010).

Article CAS Google Scholar

Gao, Z. H. et al. Fabrication, characterization and photocatalytic properties of anatase TiO2 nanoplates with exposed {001} facets. J. Nanopart. Res. 16, 1–9 (2014).

Article Google Scholar

Liu, B. & Aydil, E. S. Anatase TiO2 films with reactive {001} facets on transparent conductive substrate. Chem. Commun. 47, 9507–9509 (2011).

Article CAS Google Scholar

Mor, G. K., Varghese, O. K., Paulose, M., Ong, K. G. & Grimes, C. A. Fabrication of hydrogen sensors with transparent titanium oxide nanotube-array thin films as sensing elements. Thin Solid Films 496, 42–48 (2006).

Article CAS ADS Google Scholar

Pan, D. Y. et al. C-axis preferentially oriented and fully activated TiO2 nanotube arrays for lithium ion batteries and supercapacitors. J. Mater. Chem. A 2, 11454–11464 (2014).

Article CAS ADS Google Scholar

Wang, J. G., Zhang, P., Li, X., Zhu, J. & Li H. X. Synchronical pollutant degradation and H2 production on a Ti3+-doped TiO2 visible photocatalyst with dominant (001) facets. Appl. Catal. B 134–135, 198–204 (2013).

Acevedo-Peña. P., Carrera-Crespo, J. E., González, F. & González, I. Effect of heat treatment on the crystal phase composition, semiconducting properties and photoelectrocatalytic color removal efficiency of TiO2 nanotube arrays. Electrochim. Acta, 140, 564–571 (2014).

Article Google Scholar

Wu, J. M., Song, X. M., Ma, L. X. & Wei, X. D. Hydrothermal growth of multi-facet anatase spheres. J. Cryst. Growth 319, 57–63 (2011).

Article CAS ADS Google Scholar

Wu, X., Chen, Z. G., Lu, G. Q. & Wang, L. Z. Nanosized anatse TiO2 single crystals with tunable exposed (001) facets for enhanced energy conversion efficiency of dye-sensitized solar cells. Adv. Funct. Mater. 21, 4167–4172 (2011).

Article CAS Google Scholar

Xiang, Q. J., Yu, J. G. & Jaroniec, M. Tunable photocatalytic selectivity of TiO2 films consisted of flower-like microspheres with exposed {001} facets. Chem. Commun. 47, 4532–4534 (2011).

Article CAS Google Scholar

Han, X. G., Kuang, Q., Jin, M. S., Xie, Z. X. & Zheng, L. S. Synthesis of titania nanosheets with high percentage of exposed (001) facets and related photocatlytic properties. J. Am. Chem. Soc. 131, 3152–3153 (2009).

Article CAS Google Scholar

Zaban, A., Aruna, S. T., Tirosh, S., Gregg, B. A. & Mastai, Y. The effect of preparation condition of TiO2 colloids on their surface structures. J. Phys. Chem. B 104, 4130–4133 (2000).

Article CAS Google Scholar

Lazzeri, M., Vittadini, A. & Selloni, A. Structure and energetics of stoichiometric TiO2 anatse surfaces. Phys. Rev. B, 63, 1–9 (2001).

Article Google Scholar

Lazzeri, M. & Selloni, A. Strss-driven reconstruction of an oxide surface: the anatase TiO2 (001)- (1×4) surface. Phys. Rev. Lett. 87, 1–4 (2001).

Article Google Scholar

Herman, G. S., Sievers, M. R. & Gao, Y. Structure determination of the two-domain (1×4) anatase TiO2 (001) surface. Phys. Rev. Lett. 84, 3354–3357 (2000).

Article CAS ADS Google Scholar

Gong, X. Q. & Selloni, A. Reactivity of anatase TiO2 nanoparticles:The role of the minority (001) surface. J. Phys. Chem. B 109, 19560–19562 (2005).

Article CAS Google Scholar

Kennedy, G. C. Pressure-volume-temperature relations in water at elevated temperature and pressures. Am. J. Sci. 248, 540–564 (1950).

Article CAS ADS Google Scholar

Yang, H. G. & Zeng, H. C. Control of nucleation in solution growth of anatase TiO2 on glass substrate. J. Phys. Chem. B 107, 12244–12255 (2003).

Article CAS Google Scholar

Yin, H. B. et al. Hydrothermal synthesis of nanosized anatase and rutile TiO2 using amorphous phase TiO2 . J. Mater. Chem. 11, 1694–1703 (2001).

Article CAS Google Scholar

Kim, W. C., Suh, S. P., Choi, M. J., Kang, Y. S. & Kang, Y. S. Fabrication of SrTiO3-TiO2 heterojunction photoanode with enlarged pore diameter for dye-sensitized solar cells. J. Mater. Chem. A 1, 11820–11827 (2013).

Article CAS Google Scholar

Lu, K. & Wang, J. T. Crystal growth during crystallization of amorphous alloys. J. Cryst. Growth 94, 448–454 (1989).

Article CAS ADS Google Scholar

Lu, K., Wang, J., T. & Wei, W. D. A new method for synthesizing nanocrystalline alloys. J. Appl. Phys. 69, 522–524 (1991).

Article CAS ADS Google Scholar

Paramasivam, I., Macak, J. M. & Schmuki, P. Photocatalytic activity of nanotube TiO2 layers loaded with Ag and Au nanoparticles. Elctrochem. Commun. 10, 71–75 (2008).

Article CAS Google Scholar

Yang, H. S., Tan, Z. M., Liu, Y., Ma. Z. X. & Zhang, L. Hierarchical wall formation of titanium oxide nanotube arrays using anodic oxidation. IEEE. Trans. Nanotech. 12, 1037–1041 (2013).

Article CAS ADS Google Scholar

Yu, J. G., Dai, G. P. & Huang, B. B. Fabrication and characterization of visible-light-driven plasmonic photocatalyst Ag/AgCl/TiO2 nanotube arrays. J. Phys. Chem. C 113, 16394–16401 (2009).

Article CAS Google Scholar

Download references

This work was supported by the Environmentally Sustainable Management of Medical Wastes in China (Contract No. C/V/S/10/251) and the National Natural Foundation of Zhejiang Province, China (Grant No. Z4080070).

State Key Laboratory of Silicon Materials, School of Materials Science and Engineering, Zhejiang University, Zheda Road 38, Hangzhou, 310027, China

Jie Ding, Zhennan Huang, Xiaobin Zhang & Hangsheng Yang

State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, Lanzhou, 730050, China

Zhennan Huang & Shengzhong Kou

The Second Institute of Oceanography, State Oceanic Administration, Baochubei Road 36, Hangzhou, 310012, China

Jihao Zhu

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

J.D. and H.S.Y. conceived the concept and experiment. J.D. carried out the sample preparation and part of materials characterization and part of photocatalytic measurement. Z.N.H. participated in part of materials synthesis. J.H., Z.X., B.Z. and S.Z.K. participated in part of materials characterization. J.D. and H.S.Y. co-wrote the paper. All author discussed the results.

The authors declare no competing financial interests.

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/

Reprints and Permissions

Ding, J., Huang, Z., Zhu, J. et al. Low-temperature synthesis of high-ordered anatase TiO2 nanotube array films coated with exposed {001} nanofacets. Sci Rep 5, 17773 (2016). https://doi.org/10.1038/srep17773

Download citation

Received: 17 August 2015

Accepted: 04 November 2015

Published: 04 December 2015

DOI: https://doi.org/10.1038/srep17773

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Environmental Science and Pollution Research (2019)

Scientific Reports (2016)

Scientific Reports (2016)