Rational design of binder

Scientific Reports volume 5, Article number: 10617 (2015) Cite this article

One-dimensional nanocomposites of metal-oxide and noble metal were expected to present superior performance for nonenzymatic glucose detection due to its good conductivity and high catalytic activity inherited from noble metal and metal oxide respectively. As a proof of concept, we synthesized gold and copper oxide (Au/CuO) composite with unique one-dimensional nanocauliflowers structure. Due to the nature of the synthesis method, no any foreign binder was needed in keeping either Au or CuO in place. To the best of our knowledge, this is the first attempt in combining metal oxide and noble metal in a binder-free style for fabricating nonenzymatic glucose sensor. The Au/CuO nanocauliflowers with large electrochemical active surface and high electrolyte contact area would promise a wide linear range and high sensitive detection of glucose with good stability and reproducibility due to its good electrical conductivity of Au and high electrocatalytic activity of CuO.

Accurate detection of glucose level in blood is essential for clinical diagnostics in diabetes control1,2,3,4. Traditionally, glucose concentration is monitored by an amperometric system, in which glucose is enzymatically oxidized by highly selective glucose oxidase (GOx) immobilized on electrode surface and the thus-generated electrons or reaction product, hydrogen peroxide (H2O2), is subsequently measured so to determine the concentration of the glucose5,6,7,8. By the nature of enzyme, the GOx-based glucose sensor possesses selectivity, but its application is still limited due to the inherent drawbacks associated with enzyme purification, immobilization and its protection from denaturing. Moreover, the great distance between the deeply embedded flavin group (FAD) redox center of GOx and the electrode surface complicates the system and necessitates certain electron shuttles be present in the samples, which is arguably the biggest barrier that limits the sensitivity of this method9,10. To this end, nonenzymatic, direct electrocatalytic detection of glucose has recently garnered significant interest as it promises an electron-transfer-shuttle-free sensor and thus a high sensitivity and repeatability11,12.

For a successful nonenzymatic electrocatalytic detection of glucose, high conductivity and catalytic activity is required for the electrocatalyst. Among all of the candidate materials for the electrocatalyst in glucose detection, including noble metal13,14,15, metal oxide16,17,18, carbon materials19,20,21, mesoporous alloy22 and polymers23,24, noble metal and metal oxide materials have distinguished themselves. Recently, various nanostructures, such as nanorod25, nanowire26, nanotube27,28, dendritic29 and mesoporous materials30,31, have received significant attention due to their high surface area, efficient charge separation, etc., which are beneficial to many applications. Among the synthesis methods for fabricating one-dimensional nanostructures, anodization stands out owing to its versatility, one step, low-cost and more importantly seamless connection between the metal substrate and the anodized nanostructures which literally makes the so-prepared nanostructures an ideal electrode with high conductivity32,33,34,35. Generally, in a conventional electrochemical nonenzymatic sensing process, the electrocatalysts are prepared in the form of nanoparticles and are then immobilized on conductive substrates with the help from certain polymeric binders, which are usually insulating and electrochemically inactive. The presence of the polymeric binders in the conventional systems inevitably increases the series resistance, block the otherwise catalytically active sites and impede the electrolyte diffusion, ultimately leading to a significantly reduced electrocatalytic activity and poor performance of the sensors. For the above-mentioned reasons, anodized one-dimensional nanostructures can be a rational solution to the problem in the conventional systems.

In this study, we propose to utilize anodized one-dimensional nanostructure of metal-oxide and noble metal composite for nonenzymatic glucose detection. The composite of metal-oxide and noble metal is a judicious choice as it would present a good electrocatalytic performance plus conductivity and high catalytic activity inherited from noble metal and metal oxide respectively. As a proof of concept, we synthesized gold and copper oxide (Au/CuO) composite with one-dimensional nanostructure. Among the common noble metals, Au presented highly stable, conductive properties and good catalytically activity36,37, in addition, the detailed catalytic mechanism of glucose on gold substrate and operable strategy for improving selectivity and anti-interference ability have well been proposed and determined by Pasta and Cui38,39, which distinguished itself as best choice for constructing a nonenzymatic sensor. For metal oxides, the CuO was selected due to its high catalytic activity, low cost, abundance of copper in the crust of the Earth40,41 and more importantly the fact that one-dimensional CuO nanowire structure could be facilely synthesized by anodization42,43. The Au nanoparticles were decorated on the anodized CuO nanowire array with a simple photo-reduction method, taking on a unique nanocauliflowers structure. Due to the nature of the synthesis method, no any foreign binder was needed in keeping either Au or CuO in place. To the best of our knowledge, this is the first attempt in combining metal oxide and noble metal in a binder-free style for fabricating nonenzymatic glucose sensor. The Au/CuO nanocauliflowers with large electrochemical active surface and high electrolyte contact area would promise a wide linear range and high sensitive detection of glucose with good stability and reproducibility due to its good electrical conductivity of Au and high electrocatalytic activity of CuO.

The preparation procedures for Au/CuO nanocauliflower is illustrated in Fig. 1. First, he cleaned copper foil was electrochemically anodized in a conventional three-electrode system to form Cu(OH)2 nanowire arrays and then annealed at 180 °C for 1 h to convert Cu(OH)2 to CuO with the nanowire arrays well preserved. Second, the Au nanoparticles were deposited onto the CuO nanowires by a direct photocatalytic reduction of HAuCl4 in aqueous solution, forming a unique nanocauliflower structures. For comparison, Cu(OH)2, CuO and Au/Cu(OH)2 composite electrode were also prepared following otherwise the same procedure.

A schematic illustration of preparation of Au/CuO nanocauliflower composite.

Figure 2a-d present the scanning electron microscopy (SEM) images of the Cu(OH)2 nanowires, Au/Cu(OH)2 nanowires, CuO nanowires and Au/CuO nanocauliflowers respectively. As can be seen, a dense layer of the Cu(OH)2 nanowires covered the Cu foil substrate after anodization (Fig. 2a1-a3) and with the deposited Au nanoparticles on top, the Cu(OH)2 was able to maintain the uniform nanowire structures (Fig. 2b1-b3). After annealing, the bluish Cu(OH)2 nanowires turned into black CuO nanowires with somewhat rough surfaces (Fig. 2c1-c3). The length of the CuO nanowires was around 8~10 μm (Supplementary Fig. S1). The energy dispersive X-ray spectroscopy (EDS) spectra of the Au/CuO present evidence of the successful Au loading (Supplementary, Fig. S2). As shown in Fig. 2d1-d3, different from the Au/Cu(OH)2 case, for the Au/CuO, the Au fully covered the entire CuO nanowire surfaces, which may be ascribed to the rough CuO nanowire surfaces being active Au loading sites. More interestingly, there were Au nano-aggregates on top of each nanowire tips due to spatial availability, which presented a uniform nanocauliflowers structure (Supplementary, Fig. S3). It is worth mentioning that the pH of the aqueous HAuCl4 solution had a significant effect on the Au deposition and in this work, an optimized pH value of 6.5 was used in both Au/Cu(OH)2 and Au/CuO cases. It was found that a lower pH value would result in the removal of the nanowires from the copper foil substrate (Supplementary Fig. S4) while a higher pH value would fail to deposit Au on the nanowires (Supplementary Fig. S5).

SEM image.

(a) Cu(OH)2 nanowires, (b) Au/Cu(OH)2 nanowires, (c) CuO nanowires and (d) Au/CuO nanocauliflowers in various magnifications.

The crystal structures of the Cu(OH)2, Au/Cu(OH)2, CuO and Au/CuO samples were characterized and successfully confirmed by X-ray diffraction (XRD). As shown in Fig. 3, there are a weak diffraction peak at 43.3° and two strong diffraction peaks at 50.4° and 74.1° which come from the copper foil substrate (JCPDS 04-0836). For the Cu(OH)2 sample, the diffraction peaks indexed to orthorhombic Cu(OH)2 (JCPDS 80-0656) could be clearly identified. While the diffraction peaks at 35.5°, 38.7°, 61.5° and 66.2° in the CuO sample can be assigned to the (11-1), (111), (11-3) and (31-1) planes of CuO phase (JCPDS 48-1548), with no sharp peak that can be indexed to other impurities indicating high purity of the CuO. Particularly, both of the Au/Cu(OH)2 and Au/CuO samples present diffraction peaks at 38.2°, 44.3°, 64.5° and 77.5°, which can be assigned to the (111), (200), (220) and (311) planes of Au phase (JCPDS 65-2870), with the (111) plane of Au significantly overlapping with the (022) plane of Cu(OH)2 and (111) plane of CuO. The average crystalline sizes of Au were estimated from the Debye-Scherrer equation from the (200) crystal plane with 13.8 nm and 12.4 nm for Au/Cu(OH)2 and Au/CuO respectively44.

XRD patterns.

(a) Cu(OH)2, (b) Au/Cu(OH)2, (c) CuO and (d) Au/CuO.

The X-ray photoelectron spectroscopy (XPS) survey spectra of the Au/CuO clearly indicate Cu, O and Au elements, with no other impurities being determined (Supplementary Fig. S6a, b). The XPS of Cu 2p core level is presented in Fig. 4a where two peaks located at 934.0 and 954.0 eV are shown, which can be assigned to the binding energy of Cu 2p3/2 and Cu 2p1/2 respectively, indicating the presence of the Cu2+ on the sample45. In addition, two extra shake-up satellite peaks for Cu 2p3/2 and Cu 2p1/2 at 941.8 and 961.9 eV are also observed on higher binding energy side, implying the presence of an unfilled Cu 3d9 shell and thus further confirming the existence of Cu2+ on the sample surface. The core-level XPS of O 1s in Fig. 4b presents two band peaks at 529.7 and 531.2 eV, which can be ascribed to oxygen in CuO lattice and hydroxyl adsorption on its surface46. The Au 4f core level from the Au/CuO (Fig. 4c) can be fitted with two peaks at a binding energy of 84.0 and 87.7 eV, corresponding to Au 4f7/2 and Au 4f5/2 respectively, which is attributed to metallic gold Au(0)47.

High resolution XPS of Au/CuO sample.

(a) Cu 2p, (b) O 1s and (c) Au 4f.

The electrochemical properties of the Cu(OH)2, Au/Cu(OH)2, CuO and Au/CuO samples were investigated with a cyclic voltammetry (CV) method in 1.0 M NaOH solution with scan rate of 50 mV s-1 and working area of 1.0 cm2. As shown in Fig. 5a, all samples presented oxidation peak in range of 0.3 to 0.5 V, which can be attributed to the conversion of Cu(II) to Cu(III) which, once formed, may then act as electron transfer media for the oxidation of glucose48,49. Among all samples, the Au/CuO displayed the highest anodic current density and lowest oxidation potentials, implying its highest electrocatalytic performance. This result was expected due to the good conductivity of the Au nanostructures and high catalytic activity of the CuO nanowires.

Electrochemical nonenzymatic detection.

(a) Cyclic voltammograms of the Cu(OH)2, Au/Cu(OH)2, CuO and Au/CuO in 1.0 M NaOH with scan rate of 50 mV s-1; (b) linear sweep voltammograms of the Au/CuO electrode in various glucose concentrations with scan rate of 50 mV s-1 by subtracting the blank response in 1.0 M NaOH; (c) amperometric responses of the Au/CuO electrode with successive addition of glucose at 0.35 V vs Ag/AgCl, the top-left inset is current-glucose concentration calibration curve and the bottom-right inset is the calibration curve in low glucose concentrations.

A series of linear-sweep voltammograms (LSV) were recorded on the Au/CuO electrode at various concentrations of glucose and presented in Fig. 5b and in Supplementary Fig. S7, with the blank response in NaOH solution being subtracted. Clearly, with an increase in glucose concentration, the anodic current increased, peaked at 0.35 V vs Ag/AgCl before declining thereafter. As a result, the potential of 0.35 V vs Ag/AgCl was selected as sensing voltage for subsequent amperometric tests so to optimize the electrocatalytic response as well as obtain the best sensitivity. A typical current-time (I-t curve) of the Au/CuO sensor electrode was presented in Fig. 5c, which shows the Au/CuO sensor produced an excellent amperometric response with a short response time, in response to addition of glucose with different concentrations. A calibration curve was further plotted and presented in the top-left inset of Fig. 5c, which exhibited a high sensitivity of 708.7 μA mM-1 cm-2 and the calibration curve in low concentration was presented in the bottom-right inset of Fig. 5c, both of which helped to demonstrate a low detection limit of 0.3 μM (S/N = 3) and a wide linear range. The I-t curves of the Cu(OH)2, Au/Cu(OH)2, CuO and Au/CuO samples were recorded to determine their amperometric sensing properties (Supplementary Fig. S8-11) and the corresponding sensitivity, linear range and detection limit are summarized in Table 1. As expected, the Au/CuO sensor presented superior performance to others due the rational combination of the noble metal and metal-oxide within a desirable nano-framework.

The CV responses of the Au/CuO electrode at different scan rate were investigated (Fig. 6a) to confirm the redox reaction model. As presented in Fig. 6b, both anodic and cathodic peak currents varied linearly with potential scan rate in the range of 5 to 500 mV s-1, which suggested that the redox reaction is a surface-confined process50,51 and the glucose molecules were direct oxidized on the surface of composite electrode and the electron were directly transferred, without other mediators.

Electrochemical characterization.

(a) Cyclic voltammograms obtained at Au/CuO nanocauliflower electrode in presence of 1 mM glucose in 1.0 M NaOH at different scan rates, (b) the relationship between peak current with scan rate. (c) Nyquist plots of Cu(OH)2, Au/Cu(OH)2, CuO and Au/CuO samples collected at open circuit potential. (d) Anti-interference property of the Au/CuO electrode with initial addition of 1.0 mM glucose and 0.05 mM of UA, AA and DA and then again 1.0 mM gluocse, followed by addition of 0.02 mM sucrose, lactose and maltose and last addition of 1.0 mM glucose.

Electrochemical impedance spectra (EIS) measurement is a powerful tool for studying the electronic properties on the electrode interface. The EIS measurements were carried out to demonstrate the enhancement of conductivity after Au loading, covering the frequency of 105–0.1 Hz interval using an amplitude of 10 mV at the open circuit potential of the system. Fig. 6c presents Nyquist plots for the Cu(OH)2, Au/Cu(OH)2, CuO and Au/CuO samples, respectively. Semicircles in Nyquist plots convey information on charge transfer process as the diameters of the semicircles are equal to charge transfer resistance of a sample52. As depicted in Fig. 6c, the Au/CuO sample exhibited the smallest semicircular diameter, indeed confirmed the accelerated electron transfer in the presence of the Au nanostructures as the Au/CuO exhibited the lowest resistance among all samples.

Anti-interference property s another essential parameter for nonenzymatic glucose sensor as a good selectivity ensures high accuracy. The selectivity of the Au/CuO sensor was tested with various potentially interfering reagents. As shown in Fig. 6d, the addition of 1.0 mM of glucose resulted in a quick and significant current increase, whereas an addition of 0.1 mM of uric acid (UA), ascorbic acid (AA), dopamine (DA) and 0.05 mM such saccharides as sucrose, lactose and maltose did not cause observable current changes. Considering that the concentrations of these tested interfering substances in plasma are substantially lower than that of glucose53,54, the Au/CuO sensor possesses a very favorable selectivity toward glucose detection.

To further evaluate the reproducibility, five Au/CuO electrodes were investigated at 0.35 V to compare their amperometric current response and a good relative standard deviation of 1.56% was achieved, confirming the good reproducibility. In addition, the long-term stability of the Au/CuO electrodes were also tested by studying the current response intermittently in a period of 30 days and a good repeatability was found for the same glucose sample, suggesting the Au/CuO electrode is quite stable for the glucose sensing.

In summary, we have successfully synthesized the Au/CuO nanocauliflower electrode for highly sensitive nonenzymatic glucose sensing and demonstrated that the noble metal/metal oxide composite with binder-free connection present excellent electrocatalytic activity and high sensitivity. This study is the meaningful first step in exploring noble metal/metal oxide composite for nonenzymatic sensing.

All the chemicals were of analytical grade and used as purchased without further purification. Copper foil (thickness of 0.1 mm) were supplied by Hebei Jinjia Metal Materials Ltd. Co (P. R. China). HAuCl4, sodium hydroxide, glucose, dopamine, ascorbic acid, uric acid, sucrose, lactose and maltose were supplied by Macklin Inc, Shanghai, China. The Cu foil was anodized in an alkali solution (3 M NaOH) for 30 min under 10 mA cm-2 to form Cu(OH)2 nanowire. The temperature of the electrochemical cells was maintained at 25 °C for all experiments. The as-anodized nanowire was annealed at 180 oC for 1 h to converted Cu(OH)2 to CuO. The nanowire arrays were dipped into HAuCl4 solution (pH = 6.0) under simulated solar light irradiation (100 mW cm-2) for 30 min for Au deposition.

The morphologies electrodes were characterized by scanning electron microscopy (SEM, FEI, Quanta 600). The crystalline structure of the samples was analyzed by X-ray diffraction (XRD) (Bruker D8 Discover diffractometer, using Cu Kα radiation (1.540598 Å)). The chemical compositions and status were analyzed by X-ray Photoelectron Spectroscopy (XPS) with an Axis Ultra instrument (Kratos Analytical) under ultrahigh vacuum (<10−8 torr) and by using a monochromatic Al Kα X-ray source. The adventitious carbon 1 s peak was calibrated at 284.8 eV and used as an internal standard to compensate for any charging effects.

All the electrochemical measurements including cyclic voltammetry, chronoamperometry and electrochemical impedance spectroscope were performed with CHI 660E electrochemical working station in a three-electrode system with nanowire electrodes as working electrode (geometrical area in solution is 1.0 cm2), a platinum foil as the counter electrode and Ag/AgCl with saturated KCl solution as the reference electrode.

How to cite this article: Li, Z. et al. Rational design of binder-free noble metal/metal oxide arrays with nanocauliflower structure for wide linear range nonenzymatic glucose detection. Sci. Rep. 5, 10617; doi: 10.1038/srep10617 (2015).

Heller, A. & Feldman, B. Electrochemical glucose sensors and their applications in diabetes management. Chem. Rev. 108, 2482–2505 (2008).

CAS PubMed Google Scholar

Ronkainen, N. J., Halsall, H. B. & Heineman, W. R. Electrochemical biosensors. Chem. Soc. Rev. 39, 1747–1763 (2010).

CAS PubMed Google Scholar

Lang, X. Y. et al. Nanoporous gold supported cobalt oxide microelectrodes as high-performance electrochemical biosensors. Nat. Commun. 4, 2169 10.1038/ncomms3169 (2013).

Article CAS PubMed ADS Google Scholar

Su, J. et al. Personal glucose sensor for point-of-care early cancer diagnosis. Chem. Commun. 48, 6909–6911 (2012).

CAS Google Scholar

Wang, J. Electrochemical glucose biosensors. Chem. Rev. 108, 814–825 (2008).

CAS PubMed Google Scholar

Kim, D. M. et al. Electron-transfer mediator for a NAD-glucose dehydrogenase-based glucose sensor. Anal. Chem. 85, 11643–11649 (2013).

CAS PubMed Google Scholar

Tang, J. et al. Sensitive enzymatic glucose detection by TiO2 nanowire photoelectrochemical biosensors. J. Mater. Chem. A 2, 6153–6157 (2014).

CAS Google Scholar

Si, P. et al. Hierarchically structured one-dimensional TiO2 for protein immobilization, direct electrochemistry and mediator-free glucose sensing. ACS Nano 5, 7617–7626 (2011).

CAS PubMed Google Scholar

Li, J., Li, Y., Zhang, Y. & Wei, G. Highly sensitive molecularly imprinted electrochemical sensor based on the double amplification by an inorganic prussian blue catalytic polymer and the enzymatic effect of glucose oxidase. Anal. Chem. 84, 1888–1893 (2012).

CAS PubMed Google Scholar

Chen, C. et al. Recent advances in electrochemical glucose biosensors: a review. RSC Adv. 3, 4473–4491 (2013).

CAS Google Scholar

Tian, K., Prestgard, M. & Tiwari, A. A review of recent advances in nonenzymatic glucose sensors. Mater. Sci. Eng. C 41, 100–118 (2014).

CAS Google Scholar

Guo, C., Huo, H., Han, X., Xu, C. & Li, H. Ni/CdS bifunctional Ti@TiO2 core–shell nanowire electrode for high-performance nonenzymatic glucose sensing. Anal. Chem. 86, 876–883 (2014).

CAS PubMed Google Scholar

Bai, H., Han, M., Du, Y., Bao, J. & Dai, Z. Facile synthesis of porous tubular palladium nanostructures and their application in a nonenzymatic glucose sensor. Chem. Commun. 46, 1739–1741 (2010).

CAS Google Scholar

Park, S., Chung, T. D. & Kim, H. C. Nonenzymatic glucose detection using mesoporous platinum. Anal. Chem. 75, 3046–3049 (2003).

CAS PubMed Google Scholar

Ni, P. et al. Facile synthesis of Prussian blue @ gold nanocomposite for nonenzymatic detection of hydrogen peroxide. RSC Adv. 3, 15987–15992 (2013).

CAS Google Scholar

Fang, B. et al. Silver oxide nanowalls grown on Cu substrate as an enzymeless glucose sensor. ACS Appl. Mater. Interfaces 1, 2829–2834 (2009).

CAS PubMed Google Scholar

Chen, J., Zhang, W. D. & Ye, J. S. Nonenzymatic electrochemical glucose sensor based on MnO2/MWNTs nanocomposite. Electrochem. Commun. 10, 1268–1271 (2008).

CAS Google Scholar

Wu, Y., Jia, D., He, Y., Miao, Y. & Wu, H. L. Nano nickel oxide modified non-enzymatic glucose sensors with enhanced sensitivity through an electrochemical process strategy at high potential. Biosensor. Bioelectronics. 26, 2948–2952 (2011).

Google Scholar

Zhong, X., Yuan, R. & Chai, Y. In situ spontaneous reduction synthesis of spherical Pd@Cys-C60 nanoparticles and its application in nonenzymatic glucose biosensors. Chem. Commun. 48, 597–599 (2012).

CAS Google Scholar

Zhan, B. et al. Free-standing electrochemical electrode based on Ni(OH)2/3D graphene foam for nonenzymatic glucose detection. Nanoscale 6, 7424–7429 (2014).

CAS PubMed ADS Google Scholar

Ye, J. et al. Nonenzymatic glucose detection using multi-walled carbon nanotube electrodes. Electrochem. Commun. 6, 66–70 (2004).

CAS Google Scholar

Li, C., Wang, H., & Yamauchi, Y. Electrochemical Deposition of Mesoporous Pt–Au Alloy Films in Aqueous Surfactant Solutions: Towards a Highly Sensitive Amperometric Glucose Sensor. Chem. Eur. J. 19, 2242–2246 (2013).

CAS PubMed Google Scholar

Shoji, E. & Freund, M. S. Potentiometric sensors based on the inductive effect on the pKa of poly(aniline): a nonenzymatic glucose sensor. J. Am. Chem. Soc. 123, 3383–3384 (2001).

CAS PubMed Google Scholar

Lu, X. et al. Copper coralloid granule/polyaniline/reduced graphene oxide nanocomposites for nonenzymatic glucose detection. Anal. Methods 6, 4643–4651 (2014).

CAS Google Scholar

Luo, D., Wu, L. & Zhi, J. Fabrication of boron-doped diamond nanorod forest electrodes and their application in nonenzymatic amperometric glucose biosensing. ACS Nano 3, 2121–2128 (2009).

CAS PubMed Google Scholar

Zhuang, Z. et al. An improved sensitivity non-enzymatic glucose sensor based on a CuO nanowire modified Cu electrode. Analyst 133, 126–132 (2008).

CAS PubMed ADS Google Scholar

Zhang, Z., Zhang, L., Hedhili, M. N., Zhang, H. & Wang, P. Plasmonic gold nanocrystals coupled with photonic crystal seamlessly on TiO2 nanotube photoelectrodes for efficient vsible light photoelectrochemical water splitting. Nano. Lett. 13, 14–20 (2013).

CAS PubMed ADS Google Scholar

Xu, L., Yang, Q., Liu, X., Liu, J. & Sun, X. One-dimensional copper oxide nanotube arrays: biosensors for glucose detection. RSC Adv. 4, 1449–1455 (2014).

CAS Google Scholar

Li, C. & Yamauchi, Y. Facile solution synthesis of Ag@Pt core–shell nanoparticles with dendritic Pt shells. Phys. Chem. Chem. Phys. 15, 3490–3496 (2013).

CAS PubMed Google Scholar

Li, C., Sato, T. & Yamauchi, Y. Electrochemical Synthesis of One-Dimensional Mesoporous Pt Nanorods Using the Assembly of Surfactant Micelles in Confined Space. Angew. Chem. Int. Ed. 52, 8050–8053 (2013).

CAS Google Scholar

Yamauchi, Y. Field-Induced alignment controls of one-dimensional mesochannels in mesoporous materials. J. Ceram. Soc. Jpn. 121, 831–840 (2013).

CAS Google Scholar

Wang, C., Yin, L., Zhang, L. & Gao, R. Ti/TiO2 nanotube array/Ni composite electrodes for nonenzymatic amperometric glucose sensing. J. Phys. Chem. C 114, 4408–4413 (2010).

CAS Google Scholar

Yuan, S. et al. Engraving copper foil to give large-scale binder-free porous CuO arrays for a high-performance sodium-ion battery anode. Adv. Mater. 26, 2273–2279 (2014).

CAS PubMed Google Scholar

Zhang, Z. & Wu, H. Multiple band light trapping in ultraviolet, visible and near infrared regions with TiO2 based photonic materials. Chem. Commun. 50, 14179–14182 (2014).

CAS Google Scholar

Zhang, Z., Hossain, M. F. & Takahashi, T. Self-assembled hematite (α-Fe2O3) nanotube arrays for photoelectrocatalytic degradation of azo dye under simulated solar light irradiation. Appl. Catal. B: Environ 95, 423–429 (2010).

CAS Google Scholar

Li, Y., Song, Y. Y., Yang, C. & Xia, X. H. Hydrogen bubble dynamic template synthesis of porous gold for nonenzymatic electrochemical detection of glucose. Electrochem. Commun. 9, 981–988 (2007).

CAS Google Scholar

Zhu, H., Lu, X., Li, M., Shao, Y. & Zhu, Z. Nonenzymatic glucose voltammetric sensor based on gold nanoparticles/carbon nanotubes/ionic liquid nanocomposite. Talanta 79, 1446–1453 (2009).

CAS PubMed Google Scholar

Pasta, M., La Mantia, F. & Cui, Y. Mechanism of glucose electrochemical oxidation on gold surface. Electrochim. Acta. 55, 5561–5568 (2010).

CAS Google Scholar

Pasta, M., La Mantia, F. & Cui, Y. A new approach to glucose sensing at gold electrodes. Electrochem. Commun. 12, 1407–1410 (2010).

CAS Google Scholar

Ahmad, R., Vaseem, M., Tripathy, N. & Hahn, Y. B. Wide linear-range detecting nonenzymatic glucose biosensor based on CuO nanoparticles inkjet-printed on electrodes. Anal. Chem. 85, 10448–10454 (2013).

CAS PubMed Google Scholar

Sun, S. et al. Facile water-assisted synthesis of cupric oxide nanourchins and their application as nonenzymatic glucose biosensor. ACS Appl. Mater. Interfaces 5, 4429–4437 (2013).

CAS PubMed Google Scholar

Zhang, Z., Dua, R., Zhang, L., Zhang, H. & Wang, P. Carbon-layer-protected cuprous oxide nanowire arrays for efficient water reduction. ACS Nano 7, 1709–1717 (2013).

CAS PubMed Google Scholar

Zhang, Z. & Wang, P. Highly stable copper oxide composite as an effective photocathode for water splitting via a facile electrochemical synthesis strategy. J. Mater. Chem. 22, 2456–2464 (2012).

CAS Google Scholar

Zhang, Z., Hossain, M. F. & Takahashi, T. Photoelectrochemical water splitting on highly smooth and ordered TiO2 nanotube arrays for hydrogen generation. Int. J Hydrogen Energy. 35, 8528–8535 (2010).

CAS Google Scholar

Yin, M. et al. Copper Oxide Nanocrystals. J. Am. Chem. Soc. 127, 9506–9511 (2005).

CAS PubMed Google Scholar

Dar, M. A., Kim, Y. S., Kim, W. B., Sohn, J. M. & Shin, H. S. Structural and magnetic properties of CuO nanoneedles synthesized by hydrothermal method. Appl. Surf. Sci. 254, 7477–7481 (2008).

CAS ADS Google Scholar

Kruse, N. & Chenakin, S. XPS characterization of Au/TiO2 catalysts: Binding energy assessment and irradiation effects. Appl. Catal. A: Gen 391, 367–376 (2011).

CAS Google Scholar

Jiang, L. C. & Zhang, W. D. A highly sensitive nonenzymatic glucose sensor based on CuO nanoparticles-modified carbon nanotube electrode. Biosens. Bioelectron. 25, 1402–1407 (2010).

CAS PubMed Google Scholar

Zhuang, Z. et al. An improved sensitivity non-enzymatic glucose sensor based on a CuO nanowire modified Cu electrode. Analyst 133, 126–132 (2008).

CAS PubMed ADS Google Scholar

Bai, Y. F., Xu, T. B., Luong, J. H. T. & Cu, H. F. Direct electron transfer of glucose oxidase-boron doped diamond interface: A new solution for a classical problem. Anal. Chem. 86, 4910–4918 (2014).

CAS PubMed Google Scholar

Zhou, J., Liao, C., Zhang, L., Wang, Q. & Tian, Y. Molecular hydrogel-stabilized enzyme with facilitated electron transfer for determination of H2O2 Released from live cells. Anal. Chem. 86, 4395–4401 (2014).

CAS PubMed Google Scholar

Zhang, Z. et al. Preparation and photoelectrochemical properties of a hybrid electrode composed of polypyrrole encapsulated in highly ordered titanium dioxide nanotube array. Thin Solid Films 516, 8663–8667 (2008).

CAS ADS Google Scholar

Hrapovic, S. & Luong, J. H. T. Picoamperometric detection of glucose at ultrasmall platinum-based biosensors: preparation and characterization. Anal. Chem. 75, 3308–3315 (2003).

CAS PubMed Google Scholar

Li, L. M. et al. A novel nonenzymatic hydrogen peroxide sensor based on MnO2/graphene oxide nanocomposite. Talanta 82, 1637–1641 (2010).

CAS PubMed Google Scholar

Download references

Z.Z thanks to the support from “Yingcai” program of ECNU, Shanghai Pujiang Program (14PJ1403400) and National Natural Science Foundation of China (No. 21405046) and H. W thanks to the support from New Century Excellent Talent Project of the Department of Education (No. 1253-NCET004), Heilongjiang Province, P.R. China.

School of Chemistry and Molecular Engineering, East China Normal University, 500 Dongchuan Road, Shanghai, 200241, China

Zhenzhen Li, Yanmei Xin & Zhonghai Zhang

Provincial Key Laboratory of Oil & Gas Chemical Technology, College of Chemistry & Chemical Engineering, Northeast Petroleum University, Daqing, 163318, China

Hongjun Wu

Water Desalination and Reuse Center, Biological and Environmental Sciences and Engineering Division, King Abdullah University of Science and Technology, Thuwal, Saudi Arabia

Peng Wang

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

Z.Z. designed the experiments. Z.L, Y.X. and H.W. performed experiments and analyzed the data. Z.L., Z.Z. and P.W. wrote the manuscript and all authors discussed the results and commented on the manuscript.

The authors declare no competing financial interests.

This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/

Reprints and Permissions

Li, Z., Xin, Y., Zhang, Z. et al. Rational design of binder-free noble metal/metal oxide arrays with nanocauliflower structure for wide linear range nonenzymatic glucose detection. Sci Rep 5, 10617 (2015). https://doi.org/10.1038/srep10617

Download citation

Received: 15 January 2015

Accepted: 21 April 2015

Published: 12 June 2015

DOI: https://doi.org/10.1038/srep10617

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

Nano Research (2023)

Journal of Porous Materials (2023)

Scientific Reports (2022)

Scientific Reports (2021)

Journal of Materials Science: Materials in Electronics (2020)

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.